1. Oqim kuchi danoldan past haroratlar (20 darajadan past, -40 darajagacha yoki undan past)
Harorat sifatidakamayadixona harorati ostida, Q355NH ning rentabellik kuchisezilarli darajada oshadi.
Atrofda0 daraja, rentabellik kuchi odatda5-10% yuqori20 darajadan yuqori.
At-20 daraja, bo'lishi mumkin10-15% yuqorixona haroratiga qaraganda.
At-40 daraja, oqish quvvati ga oshishi mumkin15–25%20 darajaga nisbatan.
2. Oqim kuchi daxona harorati (20 daraja)
Bumos yozuvlar holatistandartlarda (GB/T 4171‑2008) belgilangan.
Belgilangan minimal oqish quvvati qalinlikka bog'liq:
355 MPa dan katta yoki unga tenguchun t 16 mm dan kam yoki unga teng
335 MPa dan katta yoki unga teng16 uchun < t 40 mm dan kam yoki unga teng
325 MPa dan katta yoki unga teng40 uchun < t 60 mm dan kam yoki unga teng
315 MPa dan katta yoki unga teng60 uchun < t 100 mm dan kam yoki unga teng
3. Oqim kuchi dao'rtacha ko'tarilgan harorat (100 darajadan 300 darajagacha)
Harorat sifatida100 darajadan yuqoriga ko'tariladi, hosil kuchiasta-sekin kamayishni boshlaydi.
At100 daraja, hosil kuchi taxminanga o'xshash yoki biroz pastroq20 darajadan yuqori.
At200 daraja, bu odatda10-20% pastroqxona harorati qiymatlaridan ko'ra.
At300 daraja, u tushishi mumkin20–35%xona harorati bilan solishtirganda.
4. Oqim kuchi dayuqori haroratlar (300 darajadan yuqori, ayniqsa > 400 darajadan)
300 darajadan yuqori, oqim kuchitezroq tushadi.
At400 daraja, rentabellik kuchi faqat bo'lishi mumkin50–65%xona harorati qiymati.
Yuqorida450-500 daraja, material sezilarli yumshatish hududiga kiradi; hosil kuchi keskin pasayadi va o'rmalash harakati muhim bo'ladi.
Trend haqida qisqacha ma'lumot
Past harorat (↓ T): Oqim kuchi ↑ (lekin qattiqlik ↓)
Xona harorati: Barqaror, standart belgilangan qiymatlar
Yuqori harorat (↑ T): Oqim kuchi ↓, ayniqsa 300 darajadan yuqori